Role of lignin and sodium carbonate on the swelling behavior of black liquor droplets during combustion
2018
AbstractA partial removal of lignin from black liquor (BL) by carbonation and lignin precipitation was studied. In lignin-lean BL droplets during combustion in a laboratory furnace at 800°C in stagnant air, the maximum swelling was decreased. This observation was interpreted as showing that the lignin content decrement is due mainly to removal of higher molar mass (HMM) lignin and that the Na2CO3content of the BL is increased. Stepwise precipitation experiments with industrial softwood and hardwood kraft BLs by carbonation (resulting in pH decrement from 13 to 9) indicated that a fraction of HMM lignin (MM >10 kDa) with a higher amount of carbohydrates precipitated more prominently and e…
Utilization of lignin powder for manufacturing self-binding HDF
2017
Abstract The preparation of self-binding lignocellulosic fibreboards has been investigated. Different high-density fibreboards (HDF) were hot-pressed based on a mixture of grey alder (Alnus incana L. Moench) wood chips processed by steam explosion auto-hydrolysis (SE) and 15% or 25% lignin content from three different industrial sources: softwood kraft lignin (SWKL), soda wheat straw lignin (SoWhStL) and hydrolysis wheat straw lignin (HWhStL). Density, thickness swelling (TS) after immersion in water for 24 h, modulus of rupture (MOR), modulus of elasticity (MOE) and strength of internal bond (IB) of the board samples were determined. The amount (15% or 25%) and moisture content (MC) (18±1%…
Lignin from steam‐exploded wood as binder in wood composites
2010
A study demonstrating the approach of zero‐waste technologies, a component of the Zero Emissions concept, and using lignin extracted from steam‐exploded wood as adhesive in hot‐pressed fibre boards and plywood to substitute phenol‐formaldehyde resins is reported. Properties of sample boards containing different amount of lignin adhesive are compared between themselves and with the EU standards for fibre boards. A strong correlation of density and form stability under humid conditions with the lignin content is found. Results of testing mechanical properties of the boards suggest that effect of lignin on mechanical strength depends on the size of particles and hot‐pressing temperature. Steam…
ChemInform Abstract: Chemometrics: An Important Tool for the Modern Chemist, an Example from Wood-Processing Chemistry.
2010
This study briefly outlines the idea of principal component analysis and cross-correlation calculations (applied chemometrics) and presents an illustrative example from wood-processing chemistry. The applicability of chemometric data analysis was demonstrated by investigating the various structural changes that take place in dissolved and degraded lignin ("kraft lignin") during laboratory-scale kraft pulping of Scots pine (Pinus sylvestris) and silver birch (Betula pendula). The structural data (31P NMR and size exclusion chromatographic data) on kraft lignin were further processed by chemometric multivariate techniques (PCA and 2DCC), confirming, for example, that the cleavage of beta-aryl…
Chemometrics: An Important Tool for the Modern Chemist, an Example from Wood-Processing Chemistry
2000
This study briefly outlines the idea of principal component analysis and cross-correlation calculations (applied chemometrics) and presents an illustrative example from wood-processing chemistry. The applicability of chemometric data analysis was demonstrated by investigating the various structural changes that take place in dissolved and degraded lignin ("kraft lignin") during laboratory-scale kraft pulping of Scots pine (Pinus sylvestris) and silver birch (Betula pendula). The structural data (31P NMR and size exclusion chromatographic data) on kraft lignin were further processed by chemometric multivariate techniques (PCA and 2DCC), confirming, for example, that the cleavage of beta-aryl…
High-Temperature Electrolysis of Kraft Lignin for Selective Vanillin Formation
2020
Lignin represents the largest renewable resource of aromatic moieties on earth and harbors a huge potential as a sustainable feedstock for the synthesis of biobased aromatic fine chemicals. Due to the complex, heterogeneous, and robust chemical structure of the biopolymer, the valorization is associated with significant challenges. Unfortunately, technical lignins, which are a large side stream of the pulp and paper industries, are mainly thermally exploited. In this study, technical Kraft lignin was selectively electrochemically depolymerized to the aroma chemical vanillin. Using electricity, toxic and/or expensive oxidizers could be replaced. The electrodegradation of Kraft lignin was per…
Chemometric investigation on structural changes in pine kraft lignin during pulping
2000
Abstract Various structural changes which take place in dissolved lignin during the laboratory-scale kraft pulping of Scots pine (Pinus sylvestris) were studied. Lignin samples were subjected to the alkaline cupric oxide oxidation and the analytical data further processed by various multivariate chemometric techniques (principal component analysis, PCA; principal component regression, PCR; and projection to latent structures, PLS). Several models applicable to the indirect measurement of common pine kraft pulp properties (i.e., total cooking yield, kappa number and ISO brightness) were produced.
Characterization of softwood and hardwood lignoboost kraft lignins with emphasis on their antioxidant activity
2014
Fractionation of softwood and hardwood LignoBoost kraft lignins, using sequential extraction with organic solvents of increasing hydrogen-bonding ability (dichloromethane, n-propanol, and methanol), was carried out. Using SEC, analytical pyrolysis, FTIR and UV/VIS spectroscopy, and chemical analytical methods, four fractions were obtained and characterized in terms of their yield, composition, functionality, lignin structural features, and antioxidant properties. In tests with free radicals (ABTS●+, DPPH●, O2●-) and the ORAC (oxygen radical absorbance capacity) assay, the high radical scavenging capacity of the lignin’s soluble fractions was demonstrated. The antioxidant activity of the fra…
Molecular Mass Distribution of Lignin from the Alkaline Pulping of Hardwood, Softwood, and Wheat Straw
2012
Abstract The behavior of lignin during kraft (hardwood, softwood, and wheat straw) and soda-AQ (wheat straw) pulping was studied, mainly in terms of delignification degree and molecular mass distribution (MMD). In the initial delignification phase (at 140°C for 15–60 min), a prominent part of the dissolved softwood kraft lignin (18–25 g/L, MM mostly > 3,000 Da) was found in the liquid phase of chip cavities, rather than in the external bulk black liquor (5–7 g/L, MM mostly < 3,000 Da). The maximum weight average MM values ( w) of the soluble lignin under conventional cooking conditions were detected for the kraft softwood (4,100 Da), and kraft birch (3,400 Da) when the degree of delignifica…
Bio-inspired consolidants derived from crystalline nanocellulose for decayed wood
2018
Abstract Novel bio-inspired materials derived from crystalline nanocellulose (CNC) have been tested as wood consolidants. A suspension of CNC, produced by acid hydrolysis of cellulose and used as such or mixed with lignin and/or siloxane derivatives (PDMS), was applied on rotted wood samples of Norway spruce. X-Ray diffraction analysis on CNC powder showed high crystallinity index. Dynamic light scattering (DLS) measurement indicated a nearly uniform particle size distribution with an average hydrodynamic diameter for pure CNC smaller than that in the mixtures. Raman and FTIR spectroscopies suggested interactions between lignin, PDMS and CNC components. The storage modulus of wood samples, …